Polyaminoamide Resin

 

GRADE
Viscosity(3) mPa‧s/℃
Amine Value (JIS)
☆THEO. A.H.E.W.
Gardner Colour
Compounding Ratio
Sp. Gr. 25/25℃
Gel Time(4)
Characteristics & Application
Technical
File
KINGMIDE 74
500~1,000/25
350±20
110
12Max.
50(2)
0.95
200Min.(2)
Civil engineering, Casting, Adhesive, Mortars.
KINGMIDE 74-KB
500~1,000/25
400±25
100
12Max.
50(2)
0.96
60Min.(2)
Civil engineering, Adhesive, Mortars, Crack injection.
KINGMIDE 74-NP
200~400/25
420±20
100
12Max.
50(2)
0.96
70Min.(2)
Civil engineering, Adhesive, Mortars, Crack injection.
KINGMIDE 300
200~600/200
97±5
500
10Max.
100(1)
0.97
7~10day(1)
Solvent based coatings with solid epoxy resins have fast tack free time and good flexibility, Hot melt adhesives.
KINGMIDE 305
50,000~70,000/40
240±5
180
10Max.
36(1) 100(2)
0.97
130Min.(2)
Coatings, Adhesive for abrasive maternals, Tar epoxy and plasticizer.
KINGMIDE 310
30,000~50,000/40
250±15
170
10Max.
34(1) 90(2)
0.97
100Min.(2)
Coatings, Adhesive for abrasive maternals, Tar epoxy and plasticizer.
KINGMIDE 308
16,000~26,000/40
355±30
130
12Max.
70(2)
0.98
155Min.(2)
Higher viscosity than KINGMIDE 315, General adhesive, Coatings.
KINGMIDE 315
8,000~12,000/40
335±15
120
10Max.
25(1) 67(2)
0.97
150Min.(2)
General adhesive, Coatings, Casting, Potting.
KINGMIDE 315-FC
12,000~18,000/40
300±25
140
12Max.
70(2)
0.97
60Min.(2)
General adhesive, Fast curing time than KINGMIDE 315-S.
KINGMIDE 315-L
1,500~3,000/25
440±20
85
10Max.
50(2)
0.97
80Min.(2)
General adhesive, Civil engineering and construction, Molding.

 

☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)

The physical properties of the cured epoxy resin system will change with different mixed ratio of the hardener.

The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.

(1)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:450~500)

(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:180~200)

(3)Brookfield RVT Type 1mPa.s=1cP。

(4)Gel Time : Total amount 100g at 20~23°C.

Softening Point : The Softening Point of KINGMIDE 300 is 45°C determined by Ring-and-Ball method.