Polyaminoamide Resin

 

GRADE
Viscosity(3) mPa‧s/℃
Amine Value (JIS)
☆THEO. A.H.E.W.
Gardner Colour
Compounding Ratio
Sp. Gr. 25/25℃
Gel Time(4)
Characteristics & Application
Technical
File
KINGMIDE 701
500~1,000/25
560±20
66
12Max.
35(2)
0.98
30Min.(2)
Concrete adhesives (including old to new concrete).
KINGMIDE 705
150~400/25
450±30
87
12Max.
45(2)
0.98
123Min.(2)
Low viscosity, Longer pot life than KINGMIDE 701, Concrete adhesive, Crack injection, Casting, Mortars.
KINGMIDE 710-SS
100~500/25
550±60
90
12Max.
50(2)
0.99
13Min.(2)
Low viscosity, Good low temperature cure and rapid build of mechanical properties, Accelerator for other curing agent.
KINGMIDE 715-A
1,000~3,000/25
290±40
120
12Max.
65(2)
0.97
Semi-gel
Mixed with KINGEPO SEP-85NA shows good toughness and good peel strength after post cure.
KINGMIDE X-220B
450~650/25
330±15
90
10Max.
50(2)
1.01
42Min.(2)
Epoxy mortar, Cure under humidity condition and low temperature shows less oily surface.
KINGMIDE X-2100
6,000~12,000/25
350±20
110
10Max.
50(2)
1.04
50Min.(2)
Low temperature cure, Under water cure, Adhesive, Lining, Colour stable system.
KINGMIDE 315-FS
10,000~18,000/40
310±20
140
12Max.
100(2)
0.97
120Min.(2)
General adhesive, Coatings, Civil engineering and construction.
KINGMIDE 507-KS
12,000~18,000/40
285±20
160
12Max.
100(2)
0.98
54Min.(2)
General adhesive, Coatings, Civil engineering and construction, Faster curing time than KINGMIDE 315-FS
TOHMIDE 210
200~600/200
100±5
475
10Max.
100(1)
0.97
7~10days(1)
Solvent based coatings with solid epoxy resins have fast tack free time and good flexibility, Hot melt adhesives.
TOHMIDE 215-X
50,000~70,000/40
245±10
175
10Max.
33(1) 100(2)
0.97
180Min.(2)
Coatings, Adhesive for abrasive materials, Tar epoxy and plasticizer.

 

☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)

The physical properties of the cured epoxy resin system will change with different mixed ratio of the hardener.

The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.

(1)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:450~500)

(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:180~200)

(3)Brookfield RVT Type 1mPa.s=1cP。

(4)Gel Time : Total amount 100g at 20~23°C.

Softening Point : The Softening Point of KINGMIDE 300 is 45°C determined by Ring-and-Ball method.