Products

Modified Polyamines

 

GRADE
Viscosity(1) mPa‧s/25℃
Amine Value (JIS)
☆THEO. A.H.E.W.
Gardner Colour
Compounding Ratio(2)
Sp. Gr. 25℃/25℃
Gel Time(3)
Characteristics & Application
Technical
File
KINGCURE 2010
1,200~2,000
415±20
82
4Max.
35~50
0.96
12Min.
Fast cure, Solvent-free coatings, Fast-setting adhesives.
KINGCURE 2040-MS
2,000~6,000
720±70
50
18Max.
20~35
1.08
16Min.
Fast-setting adhesives, Rapid development of strength under high humidity and low temperature.
KINGCURE 925
<80
460±25
60
3Max.
25~35
0.95
300Min.
Low viscosity, Long pot life, Electrical encapsulation, Casting, Laminates.
KINGCURE I-621
1,500~2,500
480±20
65
6Max.
30~40
1.02
20Min.
Fast Cure, Cold weather-curing agent for solvent free epoxy system.
KINGCURE I-631
70~170
290±15
105
7Max.
50~60
1.03
30Min.
Low viscosity, Cold weather-curing agent for solvent free epoxy system.
KINGCURE I-934
80~200
275±10
100
3Max.
45~55
1.02
120Min.
Solvent-free coatings, Self-leveling and mortar floorings,Laminates.
KINGCURE K-11
700~2,400
440±25
95
8Max.
45~55
1.04
7Min.
Fast-setting adhesives, Accelerator for other curing agent under conditions of low temperature.
KINGCURE K-863A
1,000~2,000
840±30
44
10Max.
20~30
1.06
10Min.
Fast cure, Fast-setting adhesives, Accelerator for other polyamide curing agent, Good for concrete pipe linings.
KINGCURE N-768
150~250
630±30
95
4Max.
45~55
0.97
10Min.
Coatings, Fast-setting adhesives, Cold weather patching compounds, Accelerator for other curing agent.
KINGCURE N-784
30~60
330±15
76
3Max.
35~45
0.95
140Min.
Low viscosity, Solvent-free coatings, Injection, Flooring, Adhesives, Casting, Laminates.

 

☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)

The physical properties of the cure epoxy resin system will change with different mixed ratio of the hardener.

The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.

(1)Brookfield RVT Type1 mPa‧s=1cP

(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:180~200)

(3)Gel Time : Total amount 100g at 20~23ºC.

◎ Total mixed resin : 2(g)