Products

Modified Polyamines

 

GRADE
Viscosity(1) mPa‧s/25℃
Amine Value (JIS)
☆THEO. A.H.E.W.
Gardner Colour
Compounding Ratio(2)
Sp. Gr. 25℃/25℃
Gel Time(3)
Characteristics & Application
Technical
File
FUJICURE FXM-824A
2,500~3,500
290±10
95
18Max.
45~55
1.13
20Min.
Casting, Laminates,Tar/Epoxy coatings, Flooring, Excellent chemical resistance, Low temperature cure, Any desired degree of reactivity or pot life can be obtained by mixing FXM-824A with FXM-824B.
FUJICURE FXM-824B
2,000~3,000
290±10
95
18Max.
45~55
1.12
720Min.
Casting, Laminates,Tar/Epoxy coatings, Flooring, Excellent chemical resistance, Low temperature cure, Any desired degree of reactivity or pot life can be obtained by mixing FXM-824A with FXM-824B.
FUJICURE FXK-832
2,000~5,000
375±20
80
5Max.
30~50
1.05
18Min.
Civil engineering, (Low temperature, wet surface curing type) Coatings, Lining, Adhesive.

 

☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)

The physical properties of the cure epoxy resin system will change with different mixed ratio of the hardener.

The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.

(1)Brookfield RVT Type1 mPa‧s=1cP

(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:180~200)

(3)Gel Time : Total amount 100g at 20~23ºC.

◎ Total mixed resin : 2(g)