Paint (General, Zinc-rich, Tar), Good corrosion resistance.
KINGMIDE 390-70
70±2
Toluene/Isopropanol (80/20)
170±20
250
9Max.
Z-Z4(3)
40~60(1)
Paint (General, Zinc-rich, Tar), Good corrosion resistance.
KINGMIDE 423-HPP
KINGMIDE 305
60±2
Xylene/Isobutanol (80/20)
130±20
320
9Max.
U-Y(3)
60~80(1)
Paint (Fast curing type).
KINGMIDE 581-60
60±2
Xylene/Isobutanol (75/25)
210±20
150
9Max.
H-N(3)
20~35(1) 70~90(2)
Paint (Fast curing type, High performance).
KINGMIDE X-2700
70±2
Toluene/Isobutanol (93/7)
150±10
245
7Max.
X-Z1(3)
35~60(1) 95~145(2)
High performance epoxy paint for low temperature, Wet surface, Water resistance, Tar epoxy, Good chemical resistance, Thick coating possible.
TOHMIDE 213-A
50±2
Xylene/Isobutanol (70/30)
90±10
500
9Max.
T-Y(3)
70~100(1)
Paint (Fast curing type).
TOHMIDE 215-70X
TOHMIDE 215-X
70±2
Xylene(100)
170±10
240
9Max.
T-X(3)
40~60(1)
Paint (General, Zinc-rich, Tar).
TOHMIDE 423
60±2
Xylene/Isobutanol (80/20)
145±10
255
9Max.
Z-Z3(3)
50~70(1)
Paint (Fast curing type).
TOHMIDE 437
75±2
Xylene(100)
250±15
130
9Max.
Z-Z5(3)
20~30(1) 70~90(2)
Paint (Fast curing type).
TOHMIDE 441-A
MODIFIED POLYAMIDE
84±2
Ethanol(100)
250±15
180
12Max.
3,000~6,000 /25ºC(5)
20~40(1) 100(2)
High glossy, Good corrosion resistance, Suitable for damp condition.
☆THEO.A.H.E.W=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)
The physical properties of the cured epoxy resin system will change with different mixed ratio of the hardener.
The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.
(1)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW : 450~500)
(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW : 180~200)
(3)Measured by a Gardner Bubble Viscometer at 25°C.