Waterborne Curing Agent
GRADE
Resin Content
Solvent (ratio)
Amine Value(4) (JIS)
☆THEO. A.H.E.W.
Gardner Colour
Viscosity(3) mPa‧s/25℃
Compounding Ratio
Characteristics & Application
Technical
File
FUJICURE FXI-919
76±2
Water(24±2)
190±10
200
10Max.
10,000~20,000
80~100(2)
Waterborne curing agent, Rapid cure and offers high gloss film, Civil engineering, Concrete coatings.
FUJICURE FXH-927
73±2
Water(27±2)
160±10
200
10Max.
10,000~20,000
17~25(1) 80~120(2)
Waterborne curing agent, Pot life longer than FUJICURE FXI-919 and offers good adhesion and moderate toughness film, Civil engineering, Concrete coatings.
TOHMIDE TXH-674B
68±2
Water(32±2)
225±15
200
15Max.
10,000~20,000
17~25(1) 80~120(2)
Waterborne curing agent, Rapid cure under low temperature and offers good adhesion and moderate toughness film, Civil engineering, Concrete coatings.
TOHMIDE TXS-53C
50±3
Water(50±3)
240±30
180
12Max.
3,000~12,500
80~120(2)
Waterbome curing agent, Civil engineering, Concrete coatings, Suitable for primer.
KINGCURE X-980W
80±3
Water(20±3)
210±15
200
4MAX.
10,000~20,000
80~120(2)
Waterbome curing agent, Rapid cure and offers moderate toughness and high gloss film, Civil engineering, Concrete coatings, Suitable for surface coating.
☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)
The physical properties of the cured epoxy resin system will change with different mixed ratio of the hardener.
The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.
(1)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW : 450~500).
(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW : 180~200).
(3)Brookfield RVT type.
(4)Solvent included (Water).