Polyaminoamide Resin

 

GRADE
Viscosity(3) mPa‧s/℃
Amine Value (JIS)
☆THEO. A.H.E.W.
Gardner Colour
Compounding Ratio
Sp. Gr. 25/25℃
Gel Time(4)
Characteristics & Application
Technical
File
KINGMIDE 315-S
8,000~12,000/40
335±15
120
11Max.
25(1) 67(2)
0.97
110Min.(2)
General adhesive, Faster curing time than KINGMIDE 315.
KINGMIDE 326-A
10,000~16,000/25
370±25
95
12Max.
50(2)
0.97
80Min.(2)
General adhesive, Civil engineering and construction. Faster curing time than KINGMIDE 328-A.
KINGMIDE 328-A
10,000~20,000/25
380±20
95
10Max.
50(2)
0.97
120Min.(2)
General adhesive, Civil engineering and construction, Toughness.
KINGMIDE 334
450~650/25
610±20
60
10Max.
33(2)
0.96
20Min.(2)
Solvent-less coatings, Lining, Casting, Flooring material, Mortars.
KINGMIDE 338
1,000~3,000/25
610±40
76
12Max.
40(2)
0.97
38Min.(2)
Civil engineering and construction, Concrete adhesive. (including old to new concrete)
KINGMIDE 340
400~600/25
790±20
60
12Max.
33(2)
0.96
30Min.(2)
Solvent-less coatings, Lining, Grouting, Mortars, Crack injection.
KINGMIDE 370
2,500~4,500/25
350±20
110
12Max.
50(2)
0.95
100Min.(2)
Civil engineering, Casting, Adhesive, Concrete repair.
KINGMIDE 374-L
200~400/25
550±20
65
12Max.
33(2)
0.95
40Min.(2)
Civil engineering and construction, Epoxy mortar, Crack injection.
KINGMIDE 384-S
7,000~10,000/40
300±20
170
12Max.
100(2)
0.97
30Min.(2)
General adhesive. Fast curing time than KINGMIDE 315-FC.
KINGMIDE 513-F
10,000~20,000/40
290±25
170
12Max.
100(2)
0.98
76Min.(2)
General adhesive, Coatings, Civil engineering and construction, Faster curing time than KINGMIDE 315-FS.

 

☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)

The physical properties of the cured epoxy resin system will change with different mixed ratio of the hardener.

The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.

(1)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:450~500)

(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:180~200)

(3)Brookfield RVT Type 1mPa.s=1cP。

(4)Gel Time : Total amount 100g at 20~23°C.

Softening Point : The Softening Point of KINGMIDE 300 is 45°C determined by Ring-and-Ball method.