製品紹介

Polyaminoamide Resin

 

GRADE
Viscosity(3) mPa‧s/℃
Amine Value (JIS)
☆THEO. A.H.E.W.
Gardner Colour
Compounding Ratio
Sp. Gr. 25/25℃
Gel Time(4)
Characteristics & Application
Technical
File
KINGMIDE 329-BP
11,000/25
240
142
10Max.
50 ~ 60(2)
1.01
25(2)
KINGMIDE 741-KB
250 ~ 650/25
380±25
95
10Max.
40 ~ 60(2)
0.95
149(2)
KINGMIDE TD-910
4,000 ~ 8,000/25
140±20
230
10Max.
100~ 120(2)
Hardening the next day (2)
KINGMIDE 315-KS
8,000~12,000/40
320 ± 20
120
11Max.
20~25 (1) 60~80 (2)
0.97
110Min.(2)
TOHMIDE 210
200~600/200
100±5
475
10Max.
100(1)
0.97
7~10days(1)
Solvent based coatings with solid epoxy resins have fast tack free time and good flexibility, Hot melt adhesives.
TOHMIDE 215-X
50,000~70,000/40
245±10
175
10Max.
33(1) 100(2)
0.97
180Min.(2)
Coatings, Adhesive for abrasive materials, Tar epoxy and plasticizer.
TOHMIDE 225-R
3,500~10,000/40
335±15
115
10Max.
23(1) 67(2)
0.97
150Min.(2)
Low viscosity type of TOHMIDE 225-X.
TOHMIDE 225-X
8,000~12,000/40
340±15
115
10Max.
23(1) 67(2)
0.97
150Min.(2)
General adhesive, Coatings, Casting, Potting.
TOHMIDE 225-XX
8,000~12,000/40
365±15
120
12Max.
65(2)
0.97
220Min.(2)
Longer pot life than TOHMIDE 225-X.
TOHMIDE 235-A
8,000~18,000/25
390±15
95
10Max.
54(2)
0.97
※120Min.(2)
General adhesive, Civil engineering and construction, Toughness.

 

☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)

The physical properties of the cured epoxy resin system will change with different mixed ratio of the hardener.

The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.

(1)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:450~500)

(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:180~200)

(3)Brookfield RVT Type 1mPa.s=1cP。

(4)Gel Time : Total amount 100g at 20~23°C.

Softening Point : The Softening Point of KINGMIDE 300 is 45°C determined by Ring-and-Ball method.