Low viscosity, Rapid cure at low temperature, Accelerator for other curing agent.
KINGCURE X-2001
1,200~2,500
420±20
80
8Max.
35~50
1.11
13Min.
Good for low temperature and high humidity cure, Mixed with amidoamine/polyamide for old to new concrete adhesives.
KINGCURE 100-BD
3,000~6,000
790±30
45
6Max.
20~35
1.08
18Min.
Fast setting adhesives, Cold weather patching componds, Accelerator for other polyamide and modified polyamine curing agent, Suitable for adhesives, coatings.
KINGCURE 451-P
4,000~15,000
550±30
50
18Max.
20~35
1.09
Semi-gel
Longer pot life, Hight Tg point combine with good chemical resistance after post cure, Suitable for casting, Encapsulation.
KINGCURE 515-KD
300~700
340±20
100
5Max.
45~55
1.01
18Min.
Solvent-less coatings, Adhesives, Patching, Flooring, Rapid hardening and rapid development of strength.
KINGCURE 367-KV
100~400
310±20
102
5Max.
40~60
1.05
41Min.
Low viscosity, Solvent-free coatings, Self-leveling floors, High gloss coatings, Good chemical resistance.
☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)
The physical properties of the cure epoxy resin system will change with different mixed ratio of the hardener.
The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.
(1)Brookfield RVT Type1 mPa‧s=1cP
(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:180~200)