製品紹介

Modified Polyamines

 

GRADE
Viscosity(1) mPa‧s/25℃
Amine Value (JIS)
☆THEO. A.H.E.W.
Gardner Colour
Compounding Ratio(2)
Sp. Gr. 25℃/25℃
Gel Time(3)
Characteristics & Application
Technical
File
KINGCURE 964-LP
400~1,200
295±20
95
18Max.
45~55
1.14
50Min.
Good film surface on low temperature and high humidity, General Adhesive, Solvent-free coatings, Self-leveling floors and mortar floorings.
KINGCURE 613-B
<100
280±20
100
2Max.
45~55
0.95
150Min.
Long pot life, Low viscosity, Light color, Suitable for casting,Cracking injection.
KINGCURE 800-C
10,000~20,000
250±20
180
5Max.
100
1.13
◎7Min.
5min-Fast setting adhesives, Patch repairs, Gel time slower than KINGCURE 800-S, Cheap price than KINGCURE 800-S & KINGCURE 800-F.
KINGCURE 800-F
10,000~20,000
210±20
180
5Max.
100
1.13
◎6Min.
5min-Fast setting adhesives, Patch repairs, Gel time slower than KINGCURE 800-S.
KINGCURE 800-S
10.000~20,000
80±15
180
2Max.
100
1.13
◎5Min.
5min-Fast setting adhesives, Patch repairs, Standard grade.
KINGCURE A-611
1,300~2,500
410±20
87
12Max.
40~50
1.09
7Min.
Adhesives, Concrete bonding, Rapid cure in thin films under cold and damp conditions.
KINGCURE B-131
40~70
400±20
74
2Max.
35~45
1.03
20Min.
Low viscosity, Light color, Fast cure, Excellent yellowing resistance, Mortar, Marble surface repair, Fast-setting adhesives.
KINGCURE B-311
300~700
270±10
115
2Max.
45~55
1.06
47Min.
Longer pot life, Low viscosity, Light color, Excellent yellowing resistance, Solvent-free coatings.
KINGCURE B-311SP
50~200
330±20
93
3Max.
45~55
1.06
42Min.
Low viscosity, Light color, Solvent-free coatings, Electrical encapsulation, Casting, Laminates.
KINGCURE B-312
<80
615±20
47
2Max.
20~25
0.98
22Min.
Low viscosity, Light color, Fast cure, Excellent yellowing resistance, Mortar, Marble surface repair, Fast-setting adhesives.

 

☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)

The physical properties of the cure epoxy resin system will change with different mixed ratio of the hardener.

The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.

(1)Brookfield RVT Type1 mPa‧s=1cP

(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:180~200)

(3)Gel Time : Total amount 100g at 20~23ºC.

◎ Total mixed resin : 2(g)