Modified Polyamines

 

GRADE
Viscosity(1) mPa‧s/25℃
Amine Value (JIS)
☆THEO. A.H.E.W.
Gardner Colour
Compounding Ratio(2)
Sp. Gr. 25℃/25℃
Gel Time(3)
Characteristics & Application
Technical
File
KINGCURE D-211
50~150
780±40
42
12Max.
20~35
1.04
10Min.
Low viscosity, Fast cure, Good chemical resistance, Accelerator for other polyamide and modified polyamine curing agent, Suitable for fast setting adhesives, Solvent-free coatings.
KINGCURE E-325
30~100
360±30
95
5Max.
45~55
0.97
40Min.
Low viscosity, Solvent-free coatings, Self-leveling floors, High gloss coatings, Good chemical resistance.
KINGCURE M-510
500~2,000
330±25
85
18Max.
45~55
1.13
18Min.
Low viscosity with rapid cure, Suitable for primer coating of civil engineering under high humidity and Low temperature.
KINGCURE M-510BS
300~700
280±20
95
18Max.
45~55
1.13
30Min.
Pot life longer than KINGCURE M-510.
KINGCURE M-530
200~500
300±20
95
18Max.
45~55
1.06
Semi-gel
Pot life longer than KINGCURE M-510BS.
KINGCURE T-642NA
<80
1150±70
36
4Max.
15~25
0.99
14Min.
Low viscosity, Light color, Fast-setting adhesives, Very suitable for marble surface repair.
FUJICURE 205-L
400~700
305±15
92
15Max.
45~55
1.12
15Min.
Solvent-less paint.
FUJICURE 4200
1,700~2,700
370±15
100
3Max.
50~60
0.97
110Min.
Casting (Light colour, Anti-weathering)
FUJICURE 4233
650~900
380±15
82
2Max.
40~50
0.95
50Min.
Modified cycloaliphatic amine, Lining. (Anti-weathering)
FUJICURE 5000
800~2,500
365±15
100
4Max.
50~70
1.02
65Min.
Flooring material, Primer for lining. (Wet surface type)

 

☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)

The physical properties of the cure epoxy resin system will change with different mixed ratio of the hardener.

The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.

(1)Brookfield RVT Type1 mPa‧s=1cP

(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:180~200)

(3)Gel Time : Total amount 100g at 20~23ºC.

◎ Total mixed resin : 2(g)