製品紹介

Modified Polyamines

 

GRADE
Viscosity(1) mPa‧s/25℃
Amine Value (JIS)
☆THEO. A.H.E.W.
Gardner Colour
Compounding Ratio(2)
Sp. Gr. 25℃/25℃
Gel Time(3)
Characteristics & Application
Technical
File
FUJICURE 5003
3,500~7,500
395±15
95
2Max.
40~70
1.08
50Min.
Paint (Good corrosion resistance)
FUJICURE 5003-D
1,000~2,000
325±15
120
5Max.
50~70
1.10
70Min.
Paint, Lining.
FUJICURE 5250
6,000~14,000
270±10
140
4Max.
60~80
1.10
11Min.
Lining, Flooring material. (Low temperature, Fast curing type)
FUJICURE 5260
1,000~2,000
340±15
110
4Max.
50~70
1.03
35Min.
Epoxy mortar.
FUJICURE 5300
800~1,700
395±20
95
9Max.
40~70
1.02
60Min.
Low cost type of FUJICURE 5000, Lining, Flooring material.
FUJICURE 5420
200~500
450±15
82
6Max.
40~55
1.07
15Min.
Low viscosity, Fast-setting, Civil engineering, Suitable for (Low temperature wet surface), Coating, Lining, Adhesives.
FUJICURE FX-220
1,000~2,000
400±20
80
7Max.
30~50
1.05
22Min.
Civil engineering, (Low temperature, Wet surface curing type) Coatings, Lining, Adhesive.
FUJICURE FXD-821
40~70
305±15
85
3Max.
40~50
0.95
93Min.
Adhesive, Casting, Coatings, Flooring material.
FUJICURE FXD-822
300~700
270±10
115
1Max.
50~70
1.03
45Min.
Modified cycloaliphatic amine, Solvent-free coatings, Self-leveling floor and mortars, Good colour stability and hight gloss.
FUJICURE FXM-823B
1,000~1,400
275±10
98
18Max.
45~55
1.16
43Min.
Casting, Laminates, Tar/Epoxy coatings, Flooring, Excellent chemical resistance, Low temperature cure, Any desired degree of reactivity or pot life can be obtained by mixing FXM-824A with FXM-824B.

 

☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)

The physical properties of the cure epoxy resin system will change with different mixed ratio of the hardener.

The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.

(1)Brookfield RVT Type1 mPa‧s=1cP

(2)The parts of Hardener by weight to 100 parts of Epoxy Resin (EEW:180~200)

(3)Gel Time : Total amount 100g at 20~23ºC.

◎ Total mixed resin : 2(g)